High Manganese Plate X120Mn12/Mn13
1)Good Ductility
2)High Wear Resistance
3)Excellent Impact Toughness
4)High Hardness

 High Manganese Plate X120Mn12 Hot Rolled Plates From Testeel

1.Characteristics of products

• abrasive      resistance steel

• Strong      plasticity and impact toughness

• It is      work hardening steel - the more impact and abrasion it gets the harder the      surface becomes.

• Steel      stays ductile underneath - only surface layer hardens.

• With      continued impact steel can harden to 500HB above.

• When      rolled - never brittle.

• Low      friction properties.

• Non-magnetic.

2.Standard-GB, ASTM, JIS, DIN

-American standard- ASTM A128

-Europe standard- X120Mn12

-JIS- SCMnH11

-China national standard- GB Mn13

- DIN- 1.3401

 

3.Brand name- Baosteel

 

4.Corresponding foreign brands

JIS- SCMnH11, AFNOR- Z120Mn12, DIN- 1.3401,EN- X120Mn12,ASTM-A128

 

5. Chemical composition(%)

 

Brand	C	Si	Mn	P	S
X120Mn12	0.90-1.20	0.30-0.80	12.00-14.00	≤0.035	≤0.030

 

 

6. Mechanical Properties

 

Tensile Strength	Elongation	20°C Impact Resistance	Initial Hardness(HB)	Hardness after Hardened(HB)	180°old Bending Test
≥900MPa	≥40%	ak≥50(J)	190-250	≥300	Qualified

 

7.Specifications of Product

3-5mm x 1000 x 2000mm

6-20mm x 1000-2500mm x 3000 or above 

 

8.Payment term- T/T or Irrevocable L/C at sight.

 

Welcome you to inquire about High Manganese Steel Plate X120Mn12/Mn13 Hot Rolled Plate From Testeel.